Laser beam cutting grade Salzgitter 240
Edition 11/2004
Usage
In addition to outstanding cold forming properties, special grade Salzgitter 240 is particularly suitable for laser and plasma cutting. The user of these steel grades must make sure that his calculation, design and processing methods are appropriate for the material. The forming process used must be suitable for the intended application and comply with the state of the art; it is of fundamental importance to the processing behaviour of these steel grades.
In addition to outstanding cold forming properties, special grade Salzgitter 240 is particularly suitable for laser and plasma cutting. The user of these steel grades must make sure that his calculation, design and processing methods are appropriate for the material. The forming process used must be suitable for the intended application and comply with the state of the art; it is of fundamental importance to the processing behaviour of these steel grades.
Product form
The steel is produced as hot strip, as well as sheet and heavy plate, in nominal thicknesses of 1,5 to 15 mm in widths in accordance with the Salzgitter Flachstahl delivery programme.
The steel is produced as hot strip, as well as sheet and heavy plate, in nominal thicknesses of 1,5 to 15 mm in widths in accordance with the Salzgitter Flachstahl delivery programme.
Melting form
Salzgitter 240 is melted as fine-grain steel according to the basic oxygen steel-making process.
Salzgitter 240 is melted as fine-grain steel according to the basic oxygen steel-making process.
Chemical composition in percent by weight [%] (Heat analysis)
| Grade | C | Si | Mn | P | S | Altotal |
|---|---|---|---|---|---|---|
| max. | max. | max. | max. | max. | min. | |
| Salzgitter 240 | 0,12 | 0,03 | 0,90 | 0,020 | 0,015 | 0,02 |
Mechanical properties
1) The given values apply to longitudinal samples.
2) Determined from longitudinal samples
3) BD = bending-block diameter
| Grade | Upper yield strength ReH 1) | Tensile strength Rm1) | Total elongation1) A5/A80 | Bending test2) |
|---|---|---|---|---|
| MPa | MPa | % | BD3)/mm | |
| Salzgitter 240 | 240 - 320 | 360 - 440 | ≥30 / ≥24 | 0 |
1) The given values apply to longitudinal samples.
2) Determined from longitudinal samples
3) BD = bending-block diameter
Cold forming
These low-perlite steel grades offer excellent bending, flanging, cold-bordering and folding properties in both longitudinal and transverse direction.
These low-perlite steel grades offer excellent bending, flanging, cold-bordering and folding properties in both longitudinal and transverse direction.
Welding
Provided that the general technical rules are observed, these steel grades can be welded both manually and using automatic equipment by means of all electrical welding processes. No major hardness increases appear in the heat-affected zone. Pre-heating is not necessary under normal welding conditions and down to workpiece temperatures of +5 °C. Below +5 °C, pre-heating to 150 °C is recommended. The welding wires and electrodes approved in the respective strength category must be used as filler metals.
In addition to this, the general meaning of the detailed information provided in ‘Stahl-Eisen-Werkstoffblatt’ (Iron and steel material sheet) 088 must be observed.
Provided that the general technical rules are observed, these steel grades can be welded both manually and using automatic equipment by means of all electrical welding processes. No major hardness increases appear in the heat-affected zone. Pre-heating is not necessary under normal welding conditions and down to workpiece temperatures of +5 °C. Below +5 °C, pre-heating to 150 °C is recommended. The welding wires and electrodes approved in the respective strength category must be used as filler metals.
In addition to this, the general meaning of the detailed information provided in ‘Stahl-Eisen-Werkstoffblatt’ (Iron and steel material sheet) 088 must be observed.
Thermal separation
This steel is highly suitable for all thermal separation methods. It was designed in particular for laser or plasma-beam cutting. If these procedures are applied correctly, it is possible to achieve practically burr-free material separation.
This steel is highly suitable for all thermal separation methods. It was designed in particular for laser or plasma-beam cutting. If these procedures are applied correctly, it is possible to achieve practically burr-free material separation.
Execution
| unpickled | unpickled | pickled | pickled |
| mill edge | sheared | mill edge | sheared |
| unoiled or oiled | unoiled or oiled |